GB/T 8110-2020 Wire electrodes and weld deposits for gas shielded metal arc welding of non alloy and fine grain steels English

Wire electrodes and weld deposits for gas shielded metal arc welding of non alloy and fine grain steels

1 Scope

This standard specifies the models, technical requirements, test methods, re-inspection and supply technical conditions of wire electrodes and weld deposits for gas shielded metal arc welding of non alloy and fine grain steels.

This standard is applicable to wire electrodes and weld deposits for gas shielded metal arc welding of non alloy and fine grain steels (hereinafter referred to as “welding wire") with a minimum tensile strength of the deposited metal of up to 570 MPa.

2 Normative references

The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies.

GB/T 2650 Impact test methods on welded joints (GB/T 2650-2008, ISO 9016: 2001, IDT)
GB/T 2652 Tensile test methods on weld and deposited metal (GB/T 2652-2008, ISO 5178: 2001, IDT)
GB/T 3323.1 Non-destructive testing of welds - Radiographic testing - Part 1: X- and gamma-ray techniques with film (GB/T 3323.1-2019, ISO 17636-1: 2013, MOD)
GB/T 18591 Welding - Guidance on the measurement of preheating temperature, interpass temperature and preheat maintenance temperature (GB/T 18591-2001, ISO 13916: 1996, IDT)
GB/T 25774.1 Test methods for welding consumables - Part 1: Preparation and testing of deposited metal specimens for mechanical properties in steel, nickel and nickel alloys (GB/T 25774.1-2010, ISO 15792-1: 2000, MOD)
GB/T 25775 Technical delivery conditions for welding consumables - Type of product dimensions tolerances and markings (GB/T 25775-2010, 1SO 544: 2003, MOD)
GB/T 25778 Procurement guidelines for welding consumables (GB/T 25778-2010, ISO 14344: 2010, MOD)
GB/T 37910.1-2019 Non-destructive testing of welds - Acceptance levels for radiographic testing - Part 1: Steel, nickel, titanium and their alloys (ISO 10675-1: 2016, MOD)
GB/T 39255-2020 Gases and gas mixtures for welding and cutting processes (ISO 14175: 2008, MOD)

3 Models

3.1 Model classification

The models of welding wires shall be classified according to the mechanical properties of deposited metal, post-weld state, the type of shielding gas and the chemical composition of welding wires. Refer to Annex C for comparison of solid welding wire models of this standard with other relevant standards.

3.2 Model preparation method

Welding wire model consists of five parts:

1) Part I: solid welding wire for gas shielded metal arc welding expressed by “G”;

2) Part II: symbol indicating the tensile strength of the deposited metal in either the as-welded or post-weld heat-treated condition, see Table 1;

3) Part III: symbol indicating the test temperature when the impact absorbed energy (KV2) is not less than 27J, see Table 2;

4) Part IV: symbol indicating the shielding gas used, which is in accordance with the provisions of GB/T 39255;

5) Part V: classification of chemical composition of welding wire, see 4.3.

In addition to the above-mentioned mandatory symbols, optional symbols may be added to the model:

a) The addition of the letter “U”, immediately after the third part, indicates that the impact absorbed energy (KV2) shall not be less than 47 J at the specified test temperature;

b) The addition of the symbol “N” for “non copper plated”, immediately after the fifth part, indicates non-copper plated welding wires.

For the purpose of this standard, the examples of welding wire models are as follows.

Foreword i
1 Scope
2 Normative references
3 Models
4 Technical requirements
5 Test methods
6 Re-inspection
7 Supply technical conditions
Annex A (Informative) Structural changes of this standard with respect to ISO 14341: 2010
Annex B (Informative) Technical differences between this standard and ISO 14341: 2010 and their causes
Annex C (Informative) Comparison of welding wire models