GB/T 35467-2017 in English

《GB/T 35467-2017湿铺防水卷材》由TC195（全国轻质与装饰装修建筑材料标准化技术委员会）归口，TC195SC1（全国轻质与装饰装修建筑材料标准化技术委员会建筑防水材料分会）执行，主管部门为中国建筑材料联合会。

ChinaStandards.net is in charge of this English translation. In case of any doubt about the English translation, the Chinese original shall be considered authoritative.

This standard is developed in accordance with the rules given in GB/T 1.1-2009.

This standard is proposed by China Building Materials Federation.

This standard is under the jurisdiction of SAC/TC 195 the National Technical Committee on Constructional Materials and Decorative Materials of Standardization Administration of China.



Wet Installed Waterproofing Sheets

1 Scope

This standard specifies classification, requirements, test methods, inspection rules, marking, packaging, storage and transport of wet installed waterproofing sheets.

This standard is applicable to self-adhesive polymer modified bitumen waterproofing sheet bonded to concrete base course using cement paste or cement mortar.

2 Normative References

The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies.

GB/T 328.2 Test Methods for Building Sheets for Waterproofing - Part 2: Bitumen Sheets for Waterproofing - Visible Defects
GB/T 328.8 Test Methods for Building Sheets for Waterproofing - Part 8: Bitumen Sheets for Waterproofing - Tensile Properties
GB/T 328.9-2007 Test Methods for Building Sheets for Waterproofing - Part 9: Plastic and Rubber Sheets for Waterproofing - Tensile Properties
GB/T 328.10-2007 Test Methods for Building Sheets for Waterproofing - Part 10: Bitumen Plastic and Rubber Sheets for Waterproofing - Watertightness
GB/T 328.11-2007 Test Methods for Building Sheets for Waterproofing - Part 11: Bitumen Sheets for Waterproofing - Flow Resistance at Elevated Temperature
GB/T 328.14 Test Methods for Building Sheets for Waterproofing - Part 14: Bitumen Sheets for Waterproofing - Flexibility at Low Temperature
GB/T 328.20 Test Methods for Building Sheets for Waterproofing - Part 20: Bitumen Sheets for Waterproofing - Resistance to Peeling of Joints
GB/T 328.26 Test Methods for Building Sheets for Waterproofing - Part 26: Bitumen Sheets for Waterproofing - Dissoluble Composite of Membrane (Impregnated and Coated Asphalt Amount)
GB/T 529-2008 Rubber, Vulcanized or Thermoplastic - Determination of Tear Strength (Trouser, Angle and Crescent Test Pieces)
JG/T 245 Vibrating Table for Concrete Test

3 Classification

3.1 Type

Products are classified into polymer membrane-based waterproofing sheets and waterproofing sheets with polyester padding (PY type) by reinforcing materials; the polymer film-based waterproofing sheets can be subdivided into high-strength (H type) and high-elongation (E type) waterproofing sheets, with the polymer film applied to the surface or middle of the sheets.

The products are classified into single-side adhesion (S) and double-side adhesion (D) sheets by bonding surface.

3.2 Specification

Product thickness:

H type and E type: 1.5mm and 2.0mm.

PY type: 3.0mm.

Other specifications can be determined through negotiations between the Supplier and the Demander.

3.3 Identification

Products are identified in the order of name, serial No. of this standard, type, bonding surface, full thickness and area.

Example: wet installed polyester reinforced double-side adhesive waterproofing sheets with 10m2 in area and 3.0mm in thickness is identified as:

Wet installed waterproofing sheet GB/T 35467-2017-PY 3.0-10.

3.4 Purpose

Wet installed waterproofing sheets are used for non-exposed waterproofing work and are bonded to concrete base course using cement paste or cement mortar. Self-adhesive overlapping should be adopted for the sheets.

4 Requirements

4.1 Area, mass per unit area and thickness

4.1.1 The area shall not be less than 99% of the marked product area.

4.1.2 The mass per unit area and thickness of PY type product shall be in accordance with those specified in Table 1.

4.1.3 The average thickness of H and E types sheet shall not be less than the nominal value.

4.1.4 The thickness shall not be less than 1.5mm (for H and E types products) and 3.0mm (for PY type product).

Table 1 Mass Per Unit Area and Thickness of 13.0mm PY Type Product
Item Index
Mass per unit area /(kg/m3) ≥ 3.1
Thickness/mm Average ≥ 3.0
Minimum single value ≥ 2.7

4.2 Appearance

4.2.1 Rolled sheets shall be rolled tightly and evenly, with the uneven part at the end surface not exceeding 20mm.

4.2.2 When the rolled sheets are unrolled at any product temperature between 4℃~45℃, there shall be no cracks or bonded parts (with the length exceeding 10 mm) at the position 1,000mm away from the core.

4.2.3 The padding of PY type product shall be impregnated without strips which are not impregnated. The surface of H and E types sheets shall be free from mineral grains.

4.2.4 Sheet surface shall be free from hole, caking, bubble, chipped edge and gap. The glue layer shall be continuous.

4.2.5 Each roll of sheets shall have no more than 1 joint; the shorter section shall not be less than 1,000 mm; the joint shall be cut neatly and lengthened by 150mm.

4.3 Physical and mechanical properties

The physical and mechanical properties of product shall meet the requirements given in Table 2.

Table 2 Physical and Mechanical Properties of Product
S.N. Item Index
H E PY
1 Soluble content /(g/m2) ≥ - 2,100
2 Tensile property Tension/(N/50mm) ≥ 300 200 500
Elongation at the maximum tension/% ≥ 50 180 30
Phenomenon under tension No separation between glue layer and polymer film or padding
3 Tear force/N ≥ 20 25 200
4 Heat resistance (70℃, 2h) Free from flowing, drippage or sliding≤2mm
5 Flexibility at low temperature (-20℃) Free of crack
6 Watertightness (0.3MPa, 120min) Watertight
7 Peel strength between sheets (overlap edge)/(N/mm) Without treatment ≥ 1.0
Water immersion treatment ≥ 0.8
Heat treatment ≥ 0.8
8 Oil leakage/number of sheets ≤ 2
9 Persistent adhesiveness /min ≥ 30
10 Peel strength with cement mortar / ( N/mm) Without treatment ≥ 1.5
Heat treatment ≥ 1.0
11 Peel strength with cement mortar after immersed in water / ( N/mm) ≥ 1.5
12 Heat aging (80℃, 168 h) Retention rate of tension/% ≥ 90
Retention rate of elongation /% ≥ 80
Flexibility at low temperature (-18℃) Free of crack
13 Dimensional change/% ±1.0 ±1.5 ±1.5
14 Thermal stability Without bulking or flowing; the maximum edge buckle of polymer film or padding is no more than 1/4 of side length

5 Test Methods

5.1 Standard conditions

Standard curing conditions of cement mortar are: the temperature of (20±2)℃ and the relative humidity greater than or equal to 95%.

5.2 Preparation of test piece

Cut the test piece after placing for 24h at (23±2)℃. For each group of test pieces, the cutting shall be distributed uniformly in sheet width direction. For peel strength test, bulk specimen may be adopted for specimen preparation, being kept away from coil edge more than 100mm, and the trimmed test piece shall be free from burr.

See Table 3 for the dimension and quantity of H and E types sheet test pieces; see Table 4 for the dimension and quantity of PY type sheet test pieces.