GB/T 19350-2012 in English
VALIDMetallic and other inorganic coatings—Post-coating treatments of iron or steel to reduce the risk of hydrogen embrittlement
- Issued on:2012-12-31
- Implemented on:2013-10-01
- File Format:PDF
- Delivery:Via email within 1~3 business days
$117.00
《GB/T 19350-2012金属和其它无机覆盖层 为减少氢脆危险的涂覆后钢铁的处理》由TC57（全国金属与非金属覆盖层标准化技术委员会）归口，主管部门为中国机械工业联合会。
Scope
This standard specifies methods for reducing the susceptibility or degree of susceptibility to hydrogen embrittlement that may occur during the surface finishing process. The steel heat treatment procedures specified in this standard can effectively reduce the susceptibility to hydrogen embrittlement. These heat treatment procedures are performed after surface finishing, but The stress relieving heat treatment process used before any secondary conversion coating process, after the machining process but before surface finishing is specified in ISO 9587. This standard does not apply to fasteners,
Loading PDF document...
Error loading PDF. Please make sure the file is valid and try again.
We also recommend
-
GB/T 19822-2024 in English
Specification for hard anodic oxidation coatings on aluminium and its alloys
2024-06-29 -
GB/T 43497-2023 in English
Electrodeposited coatings and related finishes—Electroless Ni-P-ceramic composite coatings
2023-12-28 -
GB/T 3138-2015 in English
Metallic and other inorganic coatings―Surface treatment,metallic and other inorganic coatings―Vocabulary
2015-05-15 -
GB/T 11378-2025 in English
Metallic coatings—Measurement of coating thickness—Profilometric method
2025-10-31 -
GB/T 11379-2008 in English
Metallic coatings—Electroplated coatings of chromium for engineering purposes
2008-06-19 -
GB/T 12599-2002 in English
Metallic coatings--Electroplated coatings of tin--Specification and test methods
2002-09-01 -
GB 9800-1988 in English
Chromate conversion coatings on electroplated zinc and cadmium coatings
1988-09-05 -
GB/T 19349-2012 in English
Metallic and other inorganic coatings—Pretreatment of iron or steel to reduce the risk of hydrogen embrittlement
2012-12-31